NANOR 1.6 mm

Efficast Properties
Thermoforming conditions
Thickness 1.6 mm (1/16 Inch)
Perforation Micro
Optimum activation temperature (in water bath) 65 °C (149 °F)
Activation time (in water bath) 3 to 4 minutes
Transparent when activated Yes
Working time 1.0 to 1,5 minutes
Hardening time
1.5 to 2.0 minutes
Time to completion 9 to 10 minutes
Resistance to stretch Low
Drape High
Memory (after 200% elongation) moderate
Maximum elongation when activated 2400%
Memory (after maximum elongation) moderate
Sticks to itself when activated and wet No
Sticks to itself when activated, after drying No
Adhesion (velco strip) using heat gun N.A.
 
Mechanical properties at 21°C (70°F)
Flexural modulus 750 MPa
Elastic modulus 410 MPa
Tensile strength 14.0 MPa
Strain at break 50%
Shore D hardness 61
 
General properties
Density 1.17 g/cm3
Surface feeling Smooth
Color beige
Odor natural / clay
Fatigue Cycles +10.000 cycles
Biocompatible Yes