U-PLAST 2.4 mm
U-Plast Properties | |||
Thermoforming conditions | |||
Thickness | 2.4 mm (3/32 Inch) | ||
Perforation | 28% Micro+ | ||
Optimum activation temperature (in water bath) | 65 °C (149 °F) | ||
Activation time (in water bath) | 3 to 4 minutes | ||
Transparent when activated | Yes | ||
Working time | 1,25 to 1,75 minutes | ||
Hardening time |
3,25 to 3,75 minutes | ||
Time to completion | 15 to 16 minutes | ||
Resistance to stretch | Low | ||
Drape | High | ||
Memory (after 200% elongation) | High | ||
Maximum elongation when activated | 2400% | ||
Memory (after maximum elongation) | High | ||
Sticks to itself when activated and wet | No | ||
Sticks to itself when activated, after drying | No | ||
Adhesion (velco strip) using heat gun | N.A. | ||
Mechanical properties at 21°C (70°F) | |||
Flexural modulus | 250 MPa | ||
Elastic modulus | 200 MPa | ||
Tensile strength | 12.0 MPa | ||
Strain at break | 115% | ||
Shore D hardness | 60 | ||
General properties | |||
Density | 1.13 g/cm3 | ||
Surface feeling | Smooth | ||
Color | Soft Blue | ||
Odor | None | ||
Fatigue Cycles | > 10'000 | ||
Biocompatible | Yes |